| Mechanical properties | dry / cond | Unit | Test Standard | |
| Tensile Modulus | 2400 / 1100 | MPa | ISO 527-1/-2 | |
| Yield stress | 62 / 40 | MPa | ISO 527-1/-2 | |
| Yield strain | 5.5 / 15 | % | ISO 527-1/-2 | |
| Nominal strain at break | 25 / >50 | % | ISO 527-1/-2 | |
| Flexural Modulus | 2270 / - | MPa | ISO 178 | |
| Izod notched impact strength | ISO 180/1A | |||
| 23°C | 16 / - | kJ/m² | ||
| -40°C | 10 / - | kJ/m² |
| Thermal properties | dry / cond | Unit | Test Standard | |
| Melting temperature, 10°C/min | 260 / * | °C | ISO 11357-1/-3 | |
| Temp. of deflection under load, 1.8 MPa | 65 / * | °C | ISO 75-1/-2 | |
| Coeff. of linear therm. expansion, parallel | 90 / * | E-6/K | ISO 11359-1/-2 | |
| Coeff. of linear therm. expansion, normal | 100 / * | E-6/K | ISO 11359-1/-2 |
| Other properties | dry / cond | Unit | Test Standard | |
| Water absorption, 2mm | 1.3 / * | % | Sim. to ISO 62 | |
| Density | 1110 / - | kg/m³ | ISO 1183 | |
| Water Absorption, Immersion 24h | 1.3 / * | % | ASTM D 570 |
注塑成型
預處理
干燥推薦，如果樹脂中水分含量超過建議水平
干燥溫度=80°C
干燥時間，除濕機=2-4小時
處理含水率=<0.2％
處理
熔體溫度適=290℃
熔體溫度范圍=280-300°C
模具溫度適=70°C
模具溫度范圍=50-90°C