| ABS PA-747S 臺灣奇美實業股份有限公司 物性數據 |
| 規格級別： | 押出級 | 外觀顏色： | 鈦白 |
| 用途概述： | 電冰箱內襯 | ||
| 備注說明： | 產品特性：押出級、流動性佳 | ||
| 性能項目 | 試驗條件[狀態] | 測試方法 | 測試數據 | 數據單位 | |
| 物理性能 | 比重 | --- | ASTM D-792 | 1.03 | 23/23℃ |
| 熔體流動速率 | 200℃×5kg | ASTM D-1238 | 0.7 | g/10min | |
| 熔體流動速率 | 220℃×10kg | ASTM D-1238 | 7.5 | g/10min | |
| 機械性能 | 引張強度 | --- | ASTM D-638 | 390 | Kg/cm2 |
| 引張強度 | --- | ASTM D-638 | 5530 | lb/in2 | |
| 伸長率 | --- | ASTM D-638 | 40 | % | |
| 彎曲彈性率 | --- | ASTM D-790 | 2.1×104 | Kg/cm2 | |
| 彎曲彈性率 | --- | ASTM D-790 | 3.0×105 | lb/in2 | |
| 彎曲強度 | --- | ASTM D-790 | 620 | Kg/cm2 | |
| 彎曲強度 | --- | ASTM D-790 | 8800 | lb/in2 | |
| 洛氏硬度 | --- | ASTM D-785 | 102 | R | |
| IZOD沖擊強度 | 1/8" | ASTM D-256 | 40 | kg.cm/cm | |
| IZOD沖擊強度 | 1/8" | ASTM D-256 | 7.5 | ft.lb/in | |
| IZOD沖擊強度 | 1/4" | ASTM D-256 | 35 | kg.cm/cm | |
| IZOD沖擊強度 | 1/4" | ASTM D-256 | 6.5 | ft.lb/in | |
| 熱 性 能 | 維卡軟化點 | --- | ASTM D-1525 | 103 | ℃ |
| 維卡軟化點 | --- | ASTM D-1525 | 217 | ?H | |
| 燃燒性 | File No. E56070 UL&C-UL | --- | - | 1/16"HB | |
| 熱變形溫度 | --- | ASTM D-648 | 97(206) | ℃ | |
| 熱變形溫度 | --- | ASTM D-648 | 87(189) | ?H | |
ABS/PA-747S 臺灣奇美注塑模工藝條件:
干燥處理：ABS材料具有吸濕性，要求在加工之前進行干燥處理。建議干燥條件
為80~90C下少干燥2小時。材料溫度應保證小于0.1%。
熔化溫度：210~280C；建議溫度：245C。
模具溫度：25…70C。（模具溫度將影響塑件光潔度，溫度較低則導致光潔度較低）。
注射壓力：500~1000bar。
注射速度：中高速度。
ABS/PA-747S 臺灣奇美加工
ABS是無定形的熱塑塑料，它在一定溫度范圍內軟化而不是突然熔化。ABS稍具吸濕性，在熔化加工前應予以干燥。ABS通常以丸片形成出售，顏色為原色、預著色或混合色，也有以自然粉末形成出售。也可用濃縮色料來滿足終用戶的精確要求。各種ABS材料都易于接受常用的二次加工處理，如機加工、粘合、緊固、電鍍、涂漆等。
ABS樹脂的一個基本長處就是加工性能。ABS材料的加工操作條件范圍寬廣和具有良好的剪切稀化流動特性。很多加工形式都可選用，包括注塑、擠塑、熱成型、結構泡沫和吹塑。
相關產品推薦：長期銷售：原廠原包臺灣奇美 ABS 765B塑膠原料