PPE+PA:GTX985、GTX987、GTX679、GTX674PC、GTX4610、GTX673、GTX678、GTX8730、GTX902D、GTX975、GTX989、NX0031、應.Noryl PPO, Lexan PC, Valox PBT, Ultem PEI, Cycoloy PC/ABS, Xylex PC/PET, Xenoy PC/PBT/PET.
|
|||||||||||||||||||||||||||||||
|
NORYL GTX ? Resin GTX810
SI
|
| British
|
| Metric
|
| PDF
|
Americas: COMMERCIAL
|
|
10% Glass Reinforced PPE+PA Alloy.
|
|
Property |
|
TYPICAL PROPERTIES (1)
|
MECHANICAL
|
Value
|
Unit
|
Standard
|
Nominal Stress, yld, Type I, 5 mm/min
|
910
|
kgf/cm2
|
ASTM D 638
|
Nominal Stress, brk, Type I, 5 mm/min
|
900
|
kgf/cm2
|
ASTM D 638
|
Nominal Strain, brk, 5 mm/min
|
10
|
%
|
ASTM D 638
|
Flexural Stress, yld, 2.6 mm/min, 100 mm span
|
1580
|
kgf/cm2
|
ASTM D 790
|
Flexural Modulus, 2.6 mm/min, 100 mm span
|
40400
|
kgf/cm2
|
ASTM D 790
|
Hardness, Rockwell R
|
119
|
-
|
ASTM D 785
|
IMPACT
|
Value
|
Unit
|
Standard
|
Izod Impact, notched, 23°C
|
8
|
cm-kgf/cm
|
ASTM D 256
|
Izod Impact, notched, -30°C
|
5
|
cm-kgf/cm
|
ASTM D 256
|
THERMAL
|
Value
|
Unit
|
Standard
|
Vicat Softening Temp, Rate B/50
|
240
|
°C
|
ASTM D 1525
|
HDT, 0.45 MPa, 6.4 mm, unannealed
|
245
|
°C
|
ASTM D 648
|
HDT, 1.82 MPa, 6.4 mm, unannealed
|
210
|
°C
|
ASTM D 648
|
CTE, -20°C to 150°C, flow
|
3.96E-05 - 5.04E-05
|
1/°C
|
ASTM E 831
|
Relative Temp Index, Elec
|
50
|
°C
|
UL 746B
|
Relative Temp Index, Mech w/impact
|
50
|
°C
|
UL 746B
|
Relative Temp Index, Mech w/o impact
|
50
|
°C
|
UL 746B
|
PHYSICAL
|
Value
|
Unit
|
Standard
|
Specific Gravity
|
1.16
|
-
|
ASTM D 792
|
Density
|
1.162
|
g/cm3
|
ASTM D 792
|
Water Absorption, 50% RH, equilib
|
1
|
%
|
ASTM D 570
|
Moisture Absorption, 50% RH, 24 hrs
|
0.5
|
%
|
ASTM D 570
|
Mold Shrinkage, flow, 3.2 mm (5)
|
0.6 - 0.8
|
%
|
SABIC Method
|
Mold Shrinkage, xflow, 3.2 mm (5)
|
0.65 - 0.85
|
%
|
SABIC Method
|
ELECTRICAL
|
Value
|
Unit
|
Standard
|
Arc Resistance, Tungsten {PLC}
|
6
|
PLC Code
|
ASTM D 495
|
Hot Wire Ignition {PLC)
|
0
|
PLC Code
|
UL 746A
|
High Voltage Arc Track Rate {PLC}
|
3
|
PLC Code
|
UL 746A
|
High Ampere Arc Ign, surface {PLC}
|
0
|
PLC Code
|
UL 746A
|
Comparative Tracking Index (UL) {PLC}
|
3
|
PLC Code
|
UL 746A
|
FLAME CHARACTERISTICS
|
Value
|
Unit
|
Standard
|
UL Recognized, 94HB Flame Class Rating (3)
|
1.47
|
mm
|
UL 94
|
Source GMD, last updated:2004/08/19
|
Processing |
? Do NOT mix NORYL GTX* resin with other grades of NORYL* resins.
|
Parameter
|
Injection Molding
|
Value
|
Unit
|
Drying Temperature
|
95 - 105
|
°C
|
Drying Time
|
3 - 4
|
hrs
|
Drying Time (Cumulative)
|
8
|
hrs
|
Maximum Moisture Content
|
0.07
|
%
|
Minimum Moisture Content
|
0.02
|
%
|
Melt Temperature
|
280 - 305
|
°C
|
Nozzle Temperature
|
280 - 305
|
°C
|
Front - Zone 3 Temperature
|
275 - 305
|
°C
|
Middle - Zone 2 Temperature
|
270 - 305
|
°C
|
Rear - Zone 1 Temperature
|
265 - 305
|
°C
|
Mold Temperature
|
75 - 120
|
°C
|
Back Pressure
|
0.3 - 1.4
|
MPa
|
Screw Speed
|
20 - 100
|
rpm
|
Shot to Cylinder Size
|
30 - 50
|
%
|
Vent Depth
|
0.013 - 0.038
|
mm
|
|
|
||||||