您當前的位置： 首頁 » 供應產品 » 30%玻璃纖維PPE+PS+PA NORYL RNX130 30%玻璃纖維PPE+PS+PA NORYL RNX130
| 產品型號： |
RNX130 |
| 產品規格： |
PPE |
| 產品品牌： |
沙伯基礎創新（美國） |
沙伯基礎創新塑料 PPE+PS+PA NORYL 、GTX626、GTX810、GTX830、GTX902、GTX910、GTX918W、RNX130、中山PC,沙伯基礎PC,德國拜耳PC,日本帝人PC、
PPE+PA:GTX985、GTX987、GTX679、GTX674PC、GTX4610、GTX673、GTX678、GTX8730、GTX902D、GTX975、GTX989、NX0031、應.Noryl PPO, Lexan PC, Valox PBT, Ultem PEI, Cycoloy PC/ABS, Xylex PC/PET, Xenoy PC/PBT/PET.
|
|
|
|
|
30% glass reinforced PPE+PS+PA alloy for automotive and nonautomotive applications. Recycle grade in black/gray only.
|
|
|
|
TYPICAL PROPERTIES (1)
|
|
MECHANICAL
|
Value
|
Unit
|
Standard
|
|
Tensile Stress, yld, Type I, 5 mm/min
|
1410
|
kgf/cm2
|
ASTM D 638
|
|
Tensile Stress, brk, Type I, 5 mm/min
|
1410
|
kgf/cm2
|
ASTM D 638
|
|
Tensile Strain, yld, Type I, 5 mm/min
|
5
|
%
|
ASTM D 638
|
|
Tensile Strain, brk, Type I, 5 mm/min
|
5
|
%
|
ASTM D 638
|
|
Flexural Stress, brk, 1.3 mm/min, 50 mm span
|
1890
|
kgf/cm2
|
ASTM D 790
|
|
Flexural Stress, brk, 2.6 mm/min, 100 mm span
|
1890
|
kgf/cm2
|
ASTM D 790
|
|
Flexural Modulus, 1.3 mm/min, 50 mm span
|
82900
|
kgf/cm2
|
ASTM D 790
|
|
Flexural Modulus, 2.6 mm/min, 100 mm span
|
80100
|
kgf/cm2
|
ASTM D 790
|
|
IMPACT
|
Value
|
Unit
|
Standard
|
|
Izod Impact, unnotched, 23°C
|
54
|
cm-kgf/cm
|
ASTM D 4812
|
|
Izod Impact, notched, 23°C
|
4
|
cm-kgf/cm
|
ASTM D 256
|
|
Instrumented Impact Total Energy, 23°C
|
64
|
cm-kgf
|
ASTM D 3763
|
|
THERMAL
|
Value
|
Unit
|
Standard
|
|
HDT, 0.45 MPa, 3.2 mm, unannealed
|
251
|
°C
|
ASTM D 648
|
|
HDT, 1.82 MPa, 3.2mm, unannealed
|
229
|
°C
|
ASTM D 648
|
|
PHYSICAL
|
Value
|
Unit
|
Standard
|
|
Specific Gravity
|
1.33
|
-
|
ASTM D 792
|
|
Source GMD, last updated:1998/10/09
|
|
? Do NOT mix NORYL GTX* resin with other grades of NORYL* resins.
|
|
Parameter
|
|
Injection Molding
|
Value
|
Unit
|
|
Drying Temperature
|
95 - 105
|
°C
|
|
Drying Time
|
3 - 4
|
hrs
|
|
Drying Time (Cumulative)
|
8
|
hrs
|
|
Maximum Moisture Content
|
0.07
|
%
|
|
Minimum Moisture Content
|
0.02
|
%
|
|
Melt Temperature
|
280 - 305
|
°C
|
|
Nozzle Temperature
|
280 - 305
|
°C
|
|
Front - Zone 3 Temperature
|
275 - 305
|
°C
|
|
Middle - Zone 2 Temperature
|
270 - 305
|
°C
|
|
Rear - Zone 1 Temperature
|
265 - 305
|
°C
|
|
Mold Temperature
|
75 - 120
|
°C
|
|
Back Pressure
|
0.3 - 1.4
|
MPa
|
|
Screw Speed
|
20 - 100
|
rpm
|
|
Shot to Cylinder Size
|
30 - 50
|
%
|
|
Vent Depth
|
0.013 - 0.038
|
mm
|
|
Source GMD, last updated:1998/10/09
|
|
? Polystyrene and acrylic regrind are effective purging Materials. Use temperature range appropriate for particular purging resin.
|
|
? Regrind must also be dried. Maximum 25% regrind.
|
|
|
    