NORYL ? Resin BN9003G
SI
| British
| Metric
| PDF
Americas: COMMERCIAL
PPE+PS blend. Unfilled. Blow molding. Excellent balance of impact and surface aesthetics. Suitable for automotive exterior components including spoilers.
Property
TYPICAL PROPERTIES (1)
MECHANICAL
Value
Unit
Standard
Tensile Stress, yld, Type I, 50 mm/min
480
kgf/cm2
ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min
420
kgf/cm2
ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min
3.6
%
ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min
45
%
ASTM D 638
Tensile Modulus, 5 mm/min
22800
kgf/cm2
ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span
710
kgf/cm2
ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span
21900
kgf/cm2
ASTM D 790
Tensile Stress, yield, 50 mm/min
47
MPa
ISO 527
Tensile Stress, break, 50 mm/min
42
MPa
ISO 527
Tensile Strain, yield, 50 mm/min
3.4
%
ISO 527
Tensile Strain, break, 50 mm/min
30.4
%
ISO 527
Tensile Modulus, 1 mm/min
2170
MPa
ISO 527
Flexural Stress, yield, 2 mm/min
75
MPa
ISO 178
Flexural Modulus, 2 mm/min
2190
MPa
ISO 178
IMPACT
Value
Unit
Standard
Izod Impact, unnotched, 23°C
NB
cm-kgf/cm
ASTM D 4812
Izod Impact, notched, 23°C
32
cm-kgf/cm
ASTM D 256
Izod Impact, notched, -30°C
12
cm-kgf/cm
ASTM D 256
Instrumented Impact Total Energy, 23°C
407
cm-kgf
ASTM D 3763
Izod Impact, unnotched 80*10*4 +23°C
NB
kJ/m2
ISO 180/1U
Izod Impact, unnotched 80*10*4 -30°C
54
kJ/m2
ISO 180/1U
Izod Impact, notched 80*10*4 +23°C
25
kJ/m2
ISO 180/1A
Izod Impact, notched 80*10*4 -30°C
10
kJ/m2
ISO 180/1A
Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm
26
kJ/m2
ISO 179/1eA
Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm
12
kJ/m2
ISO 179/1eA
Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm
NB
kJ/m2
ISO 179/1eU
Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm
107
kJ/m2
ISO 179/1eU
THERMAL
Value
Unit
Standard
Vicat Softening Temp, Rate B/50
141
°C
ASTM D 1525
HDT, 0.45 MPa, 3.2 mm, unannealed
124
°C
ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed
108
°C
ASTM D 648
CTE, -40°C to 40°C, flow
8.6E-05
1/°C
ASTM E 831
CTE, -40°C to 40°C, xflow
9.5E-05
1/°C
ASTM E 831
CTE, -40°C to 40°C, flow
8.6E-05
1/°C
ISO 11359-2
CTE, -40°C to 40°C, xflow
9.5E-05
1/°C
ISO 11359-2
Ball Pressure Test, 75°C +/- 2°C
N/A
-
IEC 60695-10-2
Vicat Softening Temp, Rate B/50
127
°C
ISO 306
Vicat Softening Temp, Rate B/120
130
°C
ISO 306
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm
126
°C
ISO 75/Bf
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm
110
°C
ISO 75/Af
PHYSICAL
Value
Unit
Standard
Specific Gravity
1.06
-
ASTM D 792
Mold Shrinkage on Tensile Bar, flow (2) (5)
0.55 - 0.75
%
SABIC Method
Mold Shrinkage, flow, 3.2 mm (5)
0.55 - 0.75
%
SABIC Method
Mold Shrinkage, xflow, 3.2 mm (5)
0.55 - 0.75
%
SABIC Method
Melt Flow Rate, 280°C/5.0 kgf
10
g/10 min
ASTM D 1238
Density
1.06
g/cm3
ISO 1183
Water Absorption, (23°C/sat)
0.25
%
ISO 62
Moisture Absorption (23°C / 50% RH)
0.05
%
ISO 62
Melt Volume Rate, MVR at 280°C/5.0 kg
12
cm3/10 min
ISO 1133
Source GMD, last updated:2003/11/04
Processing
Parameter
Extrusion Blow Molding
Value
Unit
Drying Temperature
80 - 85
°C
Drying Time
2 - 4
hrs
Melt Temperature (Parison)
235 - 260
°C
Barrel - Zone 1 Temperature
225 - 260
°C
Barrel - Zone 2 Temperature
230 - 260
°C
Barrel - Zone 3 Temperature
235 - 260
°C
Barrel - Zone 4 Temperature
235 - 260
°C
Adapter - Zone 5 Temperature
235 - 260
°C
Head - Zone 6 - Top Temperature
235 - 260
°C
Head - Zone 7 - Middle Temperature
235 - 260
°C
Head - Zone 7 - Bottom Temperature
235 - 260
°C
Mold Temperature
65 - 95
°C
Die Temperature
235 - 260
°C
Compare
Contact Us
NORYL? Resin
Grades
De
BN9003G
PPE+PS blend. Unfilled. Suitable for blow molded applications. Good balance of impact and surface aesthetics for automotive exterior components like spoilers.
Datasheet
Product Data: Engineering Design Data
Auto Data: Auto Specification
EXNL1117
PPE+HIPS, Flame Retardant, UL Grade, Non-Halogen Flame Retaardant, High Flow,
Datasheet
Product Data:
Auto Data:
FXN119BK
FXN119BK is a low gloss PPE/HIPS grade with good balance of mechanical properties and heat performance with intrinsic low gloss appreance. FXN119BK is available in black only.
Datasheet
Product Data:
Auto Data:
FXN121BK
FXN121BK is an unfilled PPE/HIPS FR grade designed to possess a low gloss surface appearance. FXN121BK is available in black only.
Datasheet
Product Data:
Auto Data:
FXN121LG
FXN121LG is an unfilled PPE/HIPS FR grade designed to possess a unique low gloss surface appearance.
Datasheet
Product Data:
Auto Data:
FXN4020H
PPE+HIPS, Flame Retardant, UL Grade, Non-Halogen Flame Retaardant, High Flow,
Datasheet
Product Data:
Auto Data:
HNA055
PPE+HIPS, Autoclavable engineering thermoplastic, Impact Modified, Opaque.
Datasheet
Product Data: Engineering Design Data
Auto Data:
LS6010
PPE+HIPS, Flame Retardant, Flame retardant, Heat Stabilized, Impact Modified, Nonhalogenated, Opaque,
Datasheet
Product Data: Engineering Design Data
Auto Data:
NH4030B
PPE+HIPS, Flame Retardant, Flame retardant, Heat Stabilized, Nonhalogenated, Opaque,
Datasheet
Product Data:
Auto Data:
NH6010B
PPE+HIPS, Flame Retardant, Heat Stabilized, Impact Modified, Nonhalogenated, Low smoke emission, Opaque,
Datasheet
Product Data: Engineering Design Data
Auto Data:
NH7111E
PPE+PS, Glass Reinforced, Flame Retardant, Non-halogenated, UL94 V-1 @ 1.6 mm, UL94 V-0 @ 3.0 mm, Vicat ISO306 B/120 of 152 deg C, GWIT of 775 deg C at 1/2/3 mm, GWFI of 960 deg C at 3 mm, CTI of 400 V, limited colors
Datasheet
Product Data:
Auto Data:
RN0712
PPE+HIPS, NORYL, Flame Retardant, Non-Brominated & Non-Chlorinated Flame Retardant, Experimental,
Datasheet
Product Data:
Auto Data:
V0150B
PPE+PS, Flame Retardant, Nonhalogenated FR, UL94 V-0 at 1.5 mm, UL94 5Va at 2.0 mm, GWIT of 775°C at 1/2/3 mm.