Density 密度
ISO 1183
g/cm3
1.01
Melting temperature 熔點
DSC 2nd heating 差示掃描量熱法，第二次加熱
ISO 11357
°C
178
Temp.of deflection under load 負載變形溫度
method A 1.8 MPa
method B 0.45 MPa
ISO 75
°C
°C
50
110
Vicat softening temperature 維卡軟化點
method A 10N
method B 50 N
ISO 306
°C
170
140
linear thermal expansion 線性熱膨脹 23-55°C
ISO 11359
10-4 K-1
1.4
Flammability acc. UL94 阻燃性
1.6 mm
3.2 mm
IEC 60695
HB
HB
Water absorption 吸水率
23 °C. saturation*
23°C. 50% rel. humidity.
ISO 62
%
%
1.6
0.7
Mold shrinkage 成型收縮
in flow direction 在流動方向（縱向）
in transverse direction 在相反方向（橫向）
ISO 294-4
processing acc
ISO 1874-2
%
%
0.65
1.25
Tensile test 拉伸測試
Stress at yield 屈服應力
Strain at yield 屈服應變
Strain at break 斷裂應力
Strain at break 斷裂應變
ISO 527-1/-2
MPa
%
MPa
%
47
5
>50
Tensile modulus 拉伸模量
ISO 527-2/-1A
MPa
1400
CHARPY impact strength 23 °C
簡支梁沖擊強度 -30 °C
ISO 179/1eU
kJ/m2
kJ/m2
N
N
CHARPY notched impact 23 °C
strength 簡支梁缺口沖擊強度 -30 °C
ISO 179/1eA
kJ/m2
kJ/m2
16C
9C
Electrical properties
Relative permittivity 23°C, 100 HZ
相對介電常數 23 °C, 1 MHz
IEC 60250
3.7
3.0
Dissipation factor 23°C, 100 HZ
消耗因素 23 °C, 1 MHz
IEC 60250
10-4
10-4
450
260
electric strength
絕緣強度 K20/P50
IEC 60243-1
kV/mm
26
Comparative tracking index比較性漏電指數 CTI
Test solution A 50 drops value
IEC 60112
>600
600
Volume resistivity 體積電阻率
IEC 60093
Ω cm
1015
Electrolytic corrosion effect 電解腐蝕效應
IEC 60426
step
A1