Clear Styrenic Block Copolymer (SBC) Asaflex? 800S
SBC 日本旭化成 800 高硬度Q膠
| Grade | MFR*1 |
Flexural Modulus |
Vicat Softening Point*2 |
Haze*3 | Applications |
|---|---|---|---|---|---|
| 800S | 6 | 2250 | 96 | 3.0 | Food PackagingMedicalTransparent Molded Products |
| 805 | 10 | 1550 | 91 | 0.5 | FootwearMedicalTransparent Molded Products |
| 810 | 5 | 1400 | 83 | 1.2 | Polymer ModificationAdhesives and SealantsFootwearTransparent Molded Products |
| 815 | 6 | 1200 | 82 | 0.5 | Food PackagingPolymer Modification |
| 825 | 6 | 1200 | 82 | 0.5 | Polymer ModificationFootwearTransparent Molded Products |
| 830 | 6 | 1100 | 72 | 2.0 | Polymer ModificationTransparent Molded Products |
| Property | Test Method | Unit | Value |
|---|---|---|---|
| Density | ISO 1183 | g/cm3 | 1.02 |
| Water Absorption | ISO 062 | % | <0.1 |
| MFR 200°C, 5kg Load | ISO 1133 | g/10 min | 6 |
| Mold Shrinkage | – | % | 0.2-0.8 |
| Tensile Strength, 50 mm/min | ISO 527-1 | MPa | 41 |
| Elongation, 50 mm/min | ISO 527-1 | % | 12 |
| Flexural Strength | ISO 178 | MPa | 54 |
| Flexural Modulus | ISO 178 | MPa | 2250 |
| Rockwell Hardness | ISO 2039-2 | – | HRR 78 |
| Durometer Hardness | ISO 868 | – | HDD 75 |
|
Charpy Impact Strength* Unnotched |
ISO 179 | kJ/m2 | 23 |
|
Charpy Impact Strength* V-notched |
ISO 179 | kJ/m2 | 1.1 |
|
Heat DistortionTemp. Non-annealed,1.8 MPa load, 120 K/h |
ISO 75-1 | °C | 69 |
|
Vicat Softening Point 10 N Load, 50 K/h |
ISO 306 | °C | 96 |
| Total Light Transmission, 2mm Thick Plate | ISO 13468 | ％ | 90 |
| Haze, 2mm Thick Plate | ISO 14782 | MPa | 3.0 |
免責(zé)聲明：（1）以上所展示的信息由企業(yè)自行提供，內(nèi)容的真實(shí)性、準(zhǔn)確性和合法性由發(fā)布企業(yè)負(fù)責(zé)，環(huán)球塑化網(wǎng)對(duì)此不承擔(dān)任何保證責(zé)任。我們?cè)瓌t上建議您優(yōu)先選擇“塑企通”會(huì)員合作! （2）同時(shí)我們鄭重提醒各位買/賣家，交易前請(qǐng)?jiān)敿?xì)核實(shí)對(duì)方身份，切勿隨意打款或發(fā)貨，謹(jǐn)防上當(dāng)受騙。如發(fā)現(xiàn)虛假信息，請(qǐng)向環(huán)球塑化網(wǎng)舉報(bào)。