SBC Asaflex 830 日本旭化成Q膠 高透明食品級
Clear Styrenic Block Copolymer (SBC) Asaflex? 830
Asaflex? 830 has the highest flexibility among all Asaflex grades. Used as an effective impact modifier for PS.
Applications
- Polymer Modification
- Transparent Molded Products
Physical Form
- Pellet
Features and Benefits
- Flexibility
- High impact resistance
Regulations
- Regulation (EU) No 10/2011
- USP Class Ⅵ
Characteristics
| Property | Test Method | Unit | Value |
|---|---|---|---|
| Density | ISO 1183 | g/cm3 | 1.01 |
| Water Absorption | ISO 062 | % | <0.1 |
| MFR 200°C, 5kg Load | ISO 1133 | g/10 min | 6 |
| Mold Shrinkage | – | % | 0.2～0.8 |
| Tensile Strength, 50 mm/min | ISO 527-1 | MPa | 18 |
| Elongation, 50 mm/min | ISO 527-1 | % | 250 |
| Flexural Strength | ISO 178 | MPa | 21 |
| Flexural Modulus | ISO 178 | MPa | 1100 |
| Rockwell Hardness | ISO 2039-2 | – | HRR 10 |
| Durometer Hardness | ISO 868 | – | HDD 55 |
|
Charpy Impact Strength*1 Unnotched |
ISO 179 | kJ/m2 | NB*2 |
|
Charpy Impact Strength*1 V-notched |
ISO 179 | kJ/m2 | P*3 |
|
Heat DistortionTemp. Non-annealed,1.8 MPa load, 120 K/h |
ISO 75-1 | °C | 60 |
|
Vicat Softening Point 10 N Load, 50 K/h |
ISO 306 | °C | 72 |
| Total Light Transmission, 2mm Thick Plate | ISO 13468 | ％ | 89 |
| Haze, 2mm Thick Plate | ISO 14782 | MPa | 2.0 |
1Value at fracture into two or more pieces
2Non-break at 15 J
3Partial break at 15 J
Please note that all data and values are given as typical results obtained with the indicated test methods for purposes of basic reference in grade selection only, and not as any product specification or warranty of any nature, and are subject to change without notice.