PC加纖30 日本出光G-2530 用于工程配件 汽車部件
產品參數
| 性能項目 | 試驗條件[狀態] | 測試方法 | 測試數據 | 數據單位 | ||
| 基本性能 | 吸水率 | 23℃水中24h | ASTM D-570 | 0.11 | % | |
| 物理性能 | 比重 | ASTM D-792 | 1.42 | |||
| 螺線流動長度 | 3mm厚 | 出光法 | 23 | cm | ||
| 機械性能 | 引張彈性率 | ISO R-527 (ASTM D-638) | 8100(83000) | MPa(KG/cm2) | ||
| 撓曲彈性率 | ISO 178 (ASTM D-790) | 8530(8700) | MPa(KG/cm2) | |||
| 引張破壞伸率 | ISO R-527 (ASTM D-638) | 3 | % | |||
| IZOD沖擊強度 | 4mm with notch 3.2mm with notch | ISO 180 (ASTM D-256) | 15(16) | KJ/m2(kgfcm/cm2) | ||
| 洛氏硬度 | ISO 2039-2 (ASTM D-785) | M92 | ||||
| 引張破壞強度 | ISO R-527 (ASTM D-638) | 120(1200) | MPa(KG/cm2) | |||
| 撓曲強度 | ISO 178 (ASTM D-790) | 170(1700) | MPa | |||
| 電氣性能 | 誘電正接 | 60Hz | ASTM D-150 | 8×10-4 | ||
| 誘電正接 | 106Hz | ASTM D-150 | 9×10-3 | |||
| 體積固有抵抗 | ASTM D-257 | ＜1010 | Ω·cm | |||
| 誘電率 | 106Hz | ASTM D-150 | 3.45 | |||
| 絕緣破壞電壓 | 1.6mm厚 | ASTM D-149 | ＜22 | kv/mm | ||
| 誘電率 | 60Hz | ASTM D-150 | 3.40 | |||
| 耐電弧性 | ASTM D-495 | 110 | Sec | |||
| 加工性能 | 成型收縮率 | MD | ASTM D-955 | 1.5 | ||
| TD | ASTM D-955 | 6.0 | ||||
| 熱性能 | 維卡軟化點 | ISO 306 | 150 | ℃ | ||
| 線膨脹系數 | ASTM D-696 | 2.3 | ×10-5cm/cm/℃ | |||
| 燃燒性 | 1.47mm厚 | UL 94 | V-2 | |||
| 負荷撓曲溫度 | 1.80MPa,18.6kg/cm2 | ISO 75(ASTM D-648) | 144 | ℃ | ||